Standard Svensk standard · SS-EN 3528:2013

Aerospace series - Steel X2NiCoMo18-8-5 (1.6359) - Vacuum induction melted and vacuum arc remelted - Solution treated and precipitation treated - Bar - a or D ≤ 150 mm - 1 750 MPa ≤ Rm ≤ 2 000 MPa

Status: Gällande

Köp denna standard

Standard Svensk standard · SS-EN 3528:2013

Aerospace series - Steel X2NiCoMo18-8-5 (1.6359) - Vacuum induction melted and vacuum arc remelted - Solution treated and precipitation treated - Bar - a or D ≤ 150 mm - 1 750 MPa ≤ Rm ≤ 2 000 MPa
Prenumerera på standarden - Läs mer Dölj
Pris: 636 SEK
standard ikon pdf

PDF

Pris: 636 SEK
standard ikon

Papper

Pris: 1 017,60 SEK
standard ikon pdf + standard ikon

PDF + papper

Fler alternativ Färre alternativ
Provläs denna standard
Omfattning
This standard specifies the requirements relating to:
Steel X2NiCoMo18-8-5 (1.6359)
Vacuum induction melted and vacuum arc remelted
Solution treated and precipitation treated
Bar
a or D ≤ 150 mm
1 750 MPa ≤ Rm ≤ 2 000 MPa
for aerospace applications.
NOTE Other common designation:
UNS: K92890,
Marage 250,
AECMA: FE-PA95,
ASD-STAN: FE-PM2701,
AIR: E-Z2NKD18,
BS: S 162.

Ämnesområden

Stål (49.025.10)


Köp denna standard

Standard Svensk standard · SS-EN 3528:2013

Aerospace series - Steel X2NiCoMo18-8-5 (1.6359) - Vacuum induction melted and vacuum arc remelted - Solution treated and precipitation treated - Bar - a or D ≤ 150 mm - 1 750 MPa ≤ Rm ≤ 2 000 MPa
Prenumerera på standarden - Läs mer Dölj
Pris: 636 SEK
standard ikon pdf

PDF

Pris: 636 SEK
standard ikon

Papper

Pris: 1 017,60 SEK
standard ikon pdf + standard ikon

PDF + papper

Fler alternativ Färre alternativ

Produktinformation

Språk: Engelska

Framtagen av: Standardiseringsarbete utan svenskt deltagande, SIS/TK 998

Internationell titel: Aerospace series - Steel X2NiCoMo18-8-5 (1.6359) - Vacuum induction melted and vacuum arc remelted - Solution treated and precipitation treated - Bar - a or D ≤ 150 mm - 1 750 MPa ≤ Rm ≤ 2 000 MPa

Artikelnummer: STD-88716

Utgåva: 1

Fastställd: 2013-01-15

Antal sidor: 20